Ionic conduction in ammonia functionalised closo-dodecaborates MB12H11NH3 (M = Li and Na).

Metal hydroborates and their derivatives have been receiving attention as potential solid-state ion conductors for battery applications owing to their impressive electrochemical and mechanical characteristics. However, to date only a fraction of these compounds has been investigated as solid-state electrolytes. Here, MB12H11NH3 (M = Li and Na) hydroborates are synthesized and investigated as electrolyte materials for all-solid-state batteries. The room temperature α-NaB12H11NH3 was structurally solved in P212121 (a = 7.1972(3) Å, b = 9.9225(4) Å, and c = 14.5556(5) Å). It shows a polymorphic structural transition near 140 °C to cubic Fm3̄m. LiB12H11NH3 and NaB12H11NH3 exhibit cationic conductivities of σ(Li+) = 3.0 × 10-4 S cm-1 and σ(Na+) = 1.2 × 10-4 S cm-1 at 200 °C. Hydration is found to improve ionic conductivity of the hydroborates. It is presumed that modest ionic conductivities could be due to a lack of significant re-orientational dynamics in the crystal structure resulting from the presence of the bulky -NH3 group in the anion.

Producing Alkali Metal Hydrides from Hydroxides.

In this study, a novel method for producing different alkali metal hydrides (NaH, KH, RbH, and CsH) from their corresponding metal hydroxides (NaOH, KOH, RbOH, and CsOH) is presented. For the production of NaH from NaOH, a variety of metallic reducing agents (Mg, Al, Si, CaH2, Cr, Mn, and Sr) were investigated. The reactions took place in an autoclave reactor with paraffin oil at 250 °C and 14 bar of H2 pressure. Splitting the process into two steps (metal formation and hydrogenation) simplified the separation and purification for the produced metal hydride. Moreover, the study explores the potential for this method of NaH production to be used for NaBH4 production and regeneration for hydrogen export applications. This approach offers an alternative, cost-effective method for producing NaH.

Establishing ZIF-8 as a reference material for hydrogen cryoadsorption: An interlaboratory study.

Hydrogen storage by cryoadsorption on porous materials has the advantages of low material cost, safety, fast kinetics, and high cyclic stability. The further development of this technology requires reliable data on the H2 uptake of the adsorbents, however, even for activated carbons the values between different laboratories show sometimes large discrepancies. So far no reference material for hydrogen cryoadsorption is available. The metal-organic framework ZIF-8 is an ideal material possessing high thermal, chemical, and mechanical stability that reduces degradation during handling and activation. Here, we distributed ZIF-8 pellets synthesized by extrusion to 9 laboratories equipped with 15 different experimental setups including gravimetric and volumetric analyzers. The gravimetric H2 uptake of the pellets was measured at 77 K and up to 100 bar showing a high reproducibility between the different laboratories, with a small relative standard deviation of 3-4 % between pressures of 10-100 bar. The effect of operating variables like the amount of sample or analysis temperature was evaluated, remarking the calibration of devices and other correction procedures as the most significant deviation sources. Overall, the reproducible hydrogen cryoadsorption measurements indicate the robustness of the ZIF-8 pellets, which we want to propose as a reference material.

Alkali metal alkoxyborate ester salts; a contemporary look at old compounds.

Research into the use of sodium tetraalkoxyborate salts for different chemical applications including synthetic catalysis, hydrogen storage, or battery applications has been investigated, however, understanding of the structural, thermal and electrochemical properties of these salts has been lacking since the 1950s and 1960s. A review of the synthesis, as well as a thorough characterization using 1H NMR, 11B NMR, 13C{1H} NMR, FTIR, XRD, in situ XRD, DSC-TGA, RGA-MS, TPPA, and EIS has newly identified polymorphic phase changes for Na[B(OMe)4], K[B(OMe)4], Li[B(OMe)4], Na[B(OEt)4], Na[B(OBu)4], and Na[B(OiBu)4]. The crystal structure of K[B(OMe)4] was also solved in I41/a (a = 22.337(2) Å, c = 7.648(3) Å, V = 3815.6(4) Å3, ρ = 1.128(1) g cm-3). Ionic conductivity of the different salts was analyzed, however it was found that the compounds with longer alkyl chains had no measurable ionic conductivity compared to the shorter chained samples, Na[B(OMe)4] and K[B(OMe)4] with 9.6 × 10-8 S cm-1 and 1.6 × 10-7 S cm-1, at 114 °C respectively.

Stannaborates: tuning the ion conductivity of dodecaborate salts with tin substitution.

Metal substituted dodecaborate anions can be coupled with alkali metal cations to have great potential as solid-state ion conductors for battery applications. A tin atom can replace a B-H unit within an unsubstituted dodecaborate cage to produce a stable, polar divalent anion. The chemical and structural change in forming a stannaborate results in a modified crystal structure of respective group 1 metal salts, and as a result, improves the material's ion conductivity. Li2B11H11Sn shows high ion conductivity of ∼8 mS cm-1 at 130 °C, similar to the state-of-the-art LiCB11H12 at these temperatures, however, obtaining high ion conductivity at room temperature is not possible with pristine alkali metal stannaborates.

Role of π-Radical Localization on Thermally Stable Cross-Links Between Polycyclic Aromatic Hydrocarbons.

The thermal stability of cross-links between polycyclic aromatic hydrocarbons (PAHs) is critical for understanding the formation of soot pollutants, graphite, and carbon blacks. Recently, a variety of different π-radicals have been directly imaged and suggested to enable thermally stable bonding; however, a systematic study of reactivity has been lacking. In this work, we use density functional theory to study the reactivity of PAH π-radicals. The Mulliken spin densities are initially used to categorize the different classes of localization, and the bond energy is computed to determine the degree of localization required for thermal stability. The results showed that the bond energies of PAHs are strongly correlated with the calculated spin densities, but bond energies do not exist with the bond lengths due to significant rearrangement and steric effects during bond formation. A threshold for π-radical localization is suggested that will be stable in combustion and pyrolysis environments of ρMα ≥ 0.5. Finally, the formation of multicenter bonds between localized and delocalized π-radicals was investigated using the nudge elastic band (NEB) scan, and it was found that only delocalized π-radicals provided local energy minima. These results show that the localization of π-radicals is critical for the formation of thermally stable single-center bonds between aromatic radicals.

Divalent closo-monocarborane solvates for solid-state ionic conductors.

Li-ion batteries have held the dominant position in battery research for the last 30+ years. However, due to inadequate resources and the cost of necessary elements (e.g., lithium ore) in addition to safety issues concerning the components and construction, it has become more important to look at alternative technologies. Multivalent metal batteries with solid-state electrolytes are a potential option for future battery applications. The synthesis and characterisation of divalent hydrated closo-monocarborane salts - Mg[CB11H12]2·xH2O, Ca[CB11H12]2·xH2O, and Zn[CB11H12]2·xH2O - have shown potential as solid-state electrolytes. The coordination of a solvent (e.g. H2O) to the cation in these complexes shows a significant improvement in ionic conductivity, i.e. for Zn[CB11H12]2·xH2O dried at 100 °C (10-3 S cm-1 at 170 °C) and dried at 150 °C (10-5 S cm-1 at 170 °C). Solvent choice also proved important with the ionic conductivity of Mg[CB11H12]2·3en (en = ethylenediamine) being higher than that of Mg[CB11H12]2·3.1H2O (2.6 × 10-5 S cm-1 and 1.7 × 10-8 S cm-1 at 100 °C, respectively), however, the oxidative stability was lower (<1 V (Mg2+/Mg) and 1.9 V (Mg2+/Mg), respectively). Thermal characterisation of the divalent closo-monocarborane salts showed melting and desolvation, prior to high temperature decomposition.

Thermochemical energy storage in barium carbonate enhanced by iron(III) oxide.

Renewable energy requires cost effective and reliable storage to compete with fossil fuels. This study introduces a new reactive carbonate composite (RCC) where Fe2O3 is used to thermodynamically destabilise BaCO3 and reduce its decomposition temperature from 1400 °C to 850 °C, which is more suitable for thermal energy storage applications. Fe2O3 is consumed on heating to form BaFe12O19, which is a stable Fe source for promoting reversible CO2 reactions. Two reversible reaction steps were observed that corresponded to, first, the reaction between ß-BaCO3 and BaFe12O19, and second, between γ-BaCO3 and BaFe12O19. The thermodynamic parameters were determined to be ΔH = 199 ± 6 kJ mol-1 of CO2, ΔS = 180 ± 6 J K-1 mol-1 of CO2 and ΔH = 212 ± 6 kJ mol-1 of CO2, ΔS = 185 ± 7 J K-1 mol-1 of CO2, respectively, for the two reactions. Due to the low-cost and high gravimetric and volumetric energy density, the RCC is demonstrated to be a promising candidate for next generation thermal energy storage.

Na2B11H13 and Na11(B11H14)3(B11H13)4 as potential solid-state electrolytes for Na-ion batteries.

Solid-state sodium batteries have attracted great attention owing to their improved safety, high energy density, large abundance and low cost of sodium compared to the current Li-ion batteries. Sodium-boranes have been studied as potential solid-state electrolytes and the search for new materials is necessary for future battery applications. Here, a facile and cost-effective solution-based synthesis of Na2B11H13 and Na11(B11H14)3(B11H13)4 is demonstrated. Na2B11H13 presents an ionic conductivity in the order of 10-7 S cm-1 at 30 °C, but undergoes an order-disorder phase transition and reaches 10-3 S cm-1 at 100 °C, close to that of liquids and the solid-state electrolyte Na-ß-Al2O3. The formation of a mixed-anion solid-solution, Na11(B11H14)3(B11H13)4, partially stabilises the high temperature structural polymorph observed for Na2B11H13 at room temperature and it exhibits Na+ conductivity higher than its constituents (4.7 × 10-5 S cm-1 at 30 °C). Na2B11H13 and Na11(B11H14)3(B11H13)4 exhibit an oxidative stability limit of 2.1 V vs. Na+/Na.

Synthesis of closo-CB11H12- Salts Using Common Laboratory Reagents.

Lithium and sodium salts of the closo-carbadodecaborate anion [CB11H12]- have been shown to form stable solid-state electrolytes with excellent ionic conductivity for all-solid-state batteries (ASSB). However, potential commercial application is currently hindered by the difficult, low-yielding, and expensive synthetic pathways. We report a novel and cost-effective method to synthesize the [CB11H12]- anion in a 40% yield from [B11H14]-, which can be synthesized using common laboratory reagents. The method avoids the use of expensive and dangerous reagents such as NaH, decaborane, and CF3SiMe3 and shows excellent reproducibility in product yield and purity.

Thermochemical energy storage performance of zinc destabilized calcium hydride at high-temperatures.

CaH2 has 20 times the energy density of molten salts and was patented in 2010 as a potential solar thermal energy storage material. Unfortunately, its high operating temperature (>1000 °C) and corrosivity at that temperature make it challenging to use as a thermal energy storage (TES) material in concentrating solar power (CSP) plants. To overcome these practical limitations, here we propose the thermodynamic destabilization of CaH2 with Zn metal. It is a unique approach that reduces the decomposition temperature of pure CaH2 (1100 °C at 1 bar of H2 pressure) to 597 °C at 1 bar of H2 pressure. Its new decomposition temperature is closer to the required target temperature range for TES materials used in proposed third-generation high-temperature CSP plants. A three-step dehydrogenation reaction between CaH2 and Zn (1 : 3 molar ratio) was identified from mass spectrometry, temperature-programmed desorption and in situ X-ray diffraction studies. Three reaction products, CaZn13, CaZn11 and CaZn5, were confirmed from in situ X-ray diffraction studies at 190 °C, 390 °C and 590 °C, respectively. The experimental enthalpy and entropy of the second hydrogen release reaction were determined by pressure composition isotherm measurements, conducted between 565 and 614 °C, as ΔHdes = 131 ± 4 kJ mol-1 H2 and ΔSdes = 151 ± 4 J K-1 mol-1 H2. Hydrogen cycling studies of CaZn11 at 580 °C showed sufficient cycling capacity with no significant sintering occurring during heating, as confirmed by scanning electron microscopy, demonstrating its great potential as a TES material for CSP applications. Finally, a cost comparison study of known destabilized CaH2 systems was carried out to assess the commercial potential.

Thermal properties of thermochemical heat storage materials.

The thermal conductivity, thermal diffusivity and heat capacity of materials are all vital properties in the determination of the efficiency of a thermal system. However, the thermal transport properties of heat storage materials are not consistent across previous studies, and are strongly dependent on the sample composition and measurement method. A comprehensive analysis of thermal transport properties using a consistent preparation and measurement method is lacking. This study aims to provide the foundation for a detailed insight into thermochemical heat storage material properties with consistent measurement methods. The thermal transport properties of pelletised metal hydrides, carbonates and oxides were measured using the transient plane source method to provide the thermal conductivity, thermal diffusivity and heat capacity. This information is valuable in the development of energy storage and chemical processing systems that are highly dependent on the thermal conductivity of materials.

Decomposition pathway of KAlH4 altered by the addition of Al2S3.

Altering the decomposition pathway of potassium alanate, KAlH4, with aluminium sulfide, Al2S3, presents a new opportunity to release all of the hydrogen, increase the volumetric hydrogen capacity and avoid complications associated with the formation of KH and molten K. Decomposition of 6KAlH4-Al2S3 during heating under dynamic vacuum began at 185 °C, 65 °C lower than for pure KAlH4, and released 71% of the theoretical hydrogen content below 300 °C via several unknown compounds. The major hydrogen release event, centred at 276 °C, was associated with two new compounds indexed with monoclinic (a = 10.505, b = 7.492, c = 11.772 Å, ß = 122.88°) and hexagonal (a = 10.079, c = 7.429 Å) unit cells, respectively. Unlike the 6NaAlH4-Al2S3 system, the 6KAlH4-Al2S3 system did not have M3AlH6 (M = alkali metal) as one of the intermediate decomposition products nor were the final products M2S and Al observed. Decomposition performed under hydrogen pressure initially followed a similar reaction pathway to that observed during heating under vacuum but resulted in partial melting of the sample between 300 and 350 °C. The measured enthalpy of hydrogen absorption (ΔHabs) was in the range -44.5 to -51.1 kJ mol-1 H2, which is favourable for moderate temperature hydrogen applications. Although, the hydrogen capacity decreases during consecutive H2 release and uptake cycles, the presence of excess amounts of aluminium allow for further optimisation of hydrogen storage properties.

Molten metal closo-borate solvates.

Solvated lithium closo-dodecaborate, Li2B12H12 with tetrahydrofuran and acetonitrile, show unexpected melting below 150 °C. This feature has been explored to melt-infiltrate Li2B12H12 in a nanoporous SiO2 scaffold. The ionic conductivity of Li2B12H12·xACN reaches 0.08 mS cm-1 in the liquid state at 150 °C making them suitable as battery electrolytes.

Interrogation of the Effect of Polymorphism of a Metal-Organic Framework Host on the Structure of Embedded Pd Guest Nanoparticles.

Metal-organic frameworks (MOFs) are very promising host materials for nanoscale guest materials. However, some MOFs such as MIL-53 are known to undergo phase transitions which can complicate the guest particle size control. In this study, Pd nanoparticles embedded in Al-MIL-53 were synthesised via (a) electrodeposition and (b) gas-phase reduction. A thorough structural investigation revealed that each synthesis method most likely favoured a different phase of Al-MIL-53, presenting the possibility of MOF phase selection as a technique for size control of embedded nanoparticles. For the first time, we hereby report the use of pair distribution function analysis to successfully investigate the structure and morphology of guest particles embedded in a MOF host.

Thermodynamics and performance of the Mg-H-F system for thermochemical energy storage applications.

Magnesium hydride (MgH2) is a hydrogen storage material that operates at temperatures above 300 °C. Unfortunately, magnesium sintering occurs above 420 °C, inhibiting its application as a thermal energy storage material. In this study, the substitution of fluorine for hydrogen in MgH2 to form a range of Mg(HxF1-x)2 (x = 1, 0.95, 0.85, 0.70, 0.50, 0) composites has been utilised to thermodynamically stabilise the material, so it can be used as a thermochemical energy storage material that can replace molten salts in concentrating solar thermal plants. These materials have been studied by in situ synchrotron X-ray diffraction, differential scanning calorimetry, thermogravimetric analysis, temperature-programmed-desorption mass spectrometry and Pressure-Composition-Isothermal (PCI) analysis. Thermal analysis has determined that the thermal stability of Mg-H-F solid solutions increases proportionally with fluorine content, with Mg(H0.85F0.15)2 having a maximum rate of H2 desorption at 434 °C, with a practical hydrogen capacity of 4.6 ± 0.2 wt% H2 (theoretical 5.4 wt% H2). An extremely stable Mg(H0.43F0.57)2 phase is formed upon the decomposition of each Mg-H-F composition of which the remaining H2 is not released until above 505 °C. PCI measurements of Mg(H0.85F0.15)2 have determined the enthalpy (ΔHdes) to be 73.6 ± 0.2 kJ mol-1 H2 and entropy (ΔSdes) to be 131.2 ± 0.2 J K-1 mol-1 H2, which is slightly lower than MgH2 with ΔHdes of 74.06 kJ mol-1 H2 and ΔSdes = 133.4 J K-1 mol-1 H2. Cycling studies of Mg(H0.85F0.15)2 over six absorption/desorption cycles between 425 and 480 °C show an increased usable cycling temperature of ∼80 °C compared to bulk MgH2, increasing the thermal operating temperatures for technological applications.

Structural and kinetic investigation of the hydride composite Ca(BH4)2 + MgH2 system doped with NbF5 for solid-state hydrogen storage.

Designing safe, compact and high capacity hydrogen storage systems is the key step towards introducing a pollutant free hydrogen technology into a broad field of applications. Due to the chemical bonds of hydrogen-metal atoms, metal hydrides provide high energy density in safe hydrogen storage media. Reactive hydride composites (RHCs) are a promising class of high capacity solid state hydrogen storage systems. Ca(BH4)2 + MgH2 with a hydrogen content of 8.4 wt% is one of the most promising members of the RHCs. However, its relatively high desorption temperature of ∼350 °C is a major drawback to meeting the requirements for practical application. In this work, by using NbF5 as an additive, the dehydrogenation temperature of this RHC was significantly decreased. To elucidate the role of NbF5 in enhancing the desorption properties of the Ca(BH4)2 + MgH2 (Ca-RHC), a comprehensive investigation was carried out via manometric measurements, mass spectrometry, Differential Scanning Calorimetry (DSC), in situ Synchrotron Radiation-Powder X-ray Diffraction (SR-PXD), X-ray Absorption Spectroscopy (XAS), Anomalous Small-Angle X-ray Scattering (ASAXS), Scanning and Transmission Electron Microscopy (SEM, TEM) and Nuclear Magnetic Resonance (NMR) techniques.

Hydrogen Storage Materials for Mobile and Stationary Applications: Current State of the Art.

One of the limitations to the widespread use of hydrogen as an energy carrier is its storage in a safe and compact form. Herein, recent developments in effective high-capacity hydrogen storage materials are reviewed, with a special emphasis on light compounds, including those based on organic porous structures, boron, nitrogen, and aluminum. These elements and their related compounds hold the promise of high, reversible, and practical hydrogen storage capacity for mobile applications, including vehicles and portable power equipment, but also for the large scale and distributed storage of energy for stationary applications. Current understanding of the fundamental principles that govern the interaction of hydrogen with these light compounds is summarized, as well as basic strategies to meet practical targets of hydrogen uptake and release. The limitation of these strategies and current understanding is also discussed and new directions proposed.

Novel solvates M(BH4)3S(CH3)2 and properties of halide-free M(BH4)3 (M = Y or Gd).

Rare earth metal borohydrides have been proposed as materials for solid-state hydrogen storage because of their reasonably low temperature of decomposition. New synthesis methods, which provide halide-free yttrium and gadolinium borohydride, are presented using dimethyl sulfide and new solvates as intermediates. The solvates M(BH4)3S(CH3)2 (M = Y or Gd) are transformed to α-Y(BH4)3 or Gd(BH4)3 at ~140 °C as verified by thermal analysis. The monoclinic structure of Y(BH4)3S(CH3)2, space group P21/c, a = 5.52621(8), b = 22.3255(3), c = 8.0626(1) Å and ß = 100.408(1)°, is solved from synchrotron radiation powder X-ray diffraction data and consists of buckled layers of slightly distorted octahedrons of yttrium atoms coordinated to five borohydride groups and one dimethyl sulfide group. Significant hydrogen loss is observed from Y(BH4)3 below 300 °C and rehydrogenation at 300 °C and p(H2) = 1550 bar does not result in the reformation of Y(BH4)3, but instead yields YH3. Moreover, composites systems Y(BH4)3-LiBH4 1 : 1 and Y(BH4)3-LiCl 1 : 1 prepared from as-synthesised Y(BH4)3 are shown to melt at 190 and 220 °C, respectively.

Eutectic melting in metal borohydrides.

A series of monometallic borohydrides and borohydride eutectic mixtures have been investigated during thermal ramping by mass spectroscopy, differential scanning calorimetry, and photography. Mixtures of LiBH4-NaBH4, LiBH4-KBH4, LiBH4-Mg(BH4)2, LiBH4-Ca(BH4)2, LiBH4-Mn(BH4)2, NaBH4-KBH4, and LiBH4-NaBH4-KBH4 all displayed melting behaviour below that of the monometallic phases (up to 167 °C lower). Generally, each system behaves differently with respect to their physical behaviour upon melting. The molten phases can exhibit colour changes, bubbling and in some cases frothing, or even liquid-solid phase transitions during hydrogen release. Remarkably, the eutectic melt can also allow for hydrogen release at temperatures lower than that of the individual components. Some systems display decomposition of the borohydride in the solid-state before melting and certain hydrogen release events have also been linked to the adverse reaction of samples with impurities, usually within the starting reagents, and these may also be coupled with bubbling or frothing of the ionic melt.